Slider

ABSTRACT

This invention relates to a slider, which comprises a polyethylene foam skin, a laminated plastic film and a plastic sheet. The polyethylene foam skin has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm. The laminated plastic film is heat bonded to a top surface of the polyethylene foam skin entirely and the laminated plastic film has a thickness in range of 0.03 to 0.3 mm. The plastic sheet is heat bonded to a bottom of the polyethylene foam skin entirely and the plastic sheet has a thickness in range of 0.3 to 2 mm. In addition, the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film.

CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part application of co-pending U.S. application Ser. No. 10/797,094, filed Mar. 11, 2004, and also is a continuation-in-part application of co-pending U.S. application Ser. No. 10/386,634 filed, Mar. 13, 2003.

TECHNICAL FIELD

This invention relates generally to a slider, which is provided for being as sports and recreational equipment, such as snow, grass or sand sliders/sleds and sports mats as well.

BACKGROUND OF THE INVENTION

A conventional slider/sled is generally made of a foam board with a top skin, a bottom skin and steerable/gripping accessories thereon that makes the slider/sled heavy to transport and to carry. Another conventional slider/sled, namely a simple slider/sled, is made of a foam skin with gripping through holes thereon or is made of a foam skin bonded with wearable bottom skin and gripping holes thereon that indeed improves the weight and transport of the previous slider/sled.

However, patterns printed on the surfaces of the foregoing sliders/sleds are easily worn off after frequent uses of the sliders/sleds and it is also known that ultraviolet, moisture and dirt damage the structure of the foam materials of the sliders/sleds that reduces the lives of the sliders/sleds. Therefore, the sliders/sleds having enduring patterns and structures are in great demand.

SUMMARY OF INVENTION

The primary objective of the present invention is to provide a slider with lightweight and strong structure.

Another objective of the invention is to provide a laminated layer for a slider and the laminated layer comprises a foam skin and an enduring patterned plastic film.

In one embodiment, the slider of the present invention comprises a polyethylene foam skin, a laminated plastic film and a plastic sheet. The polyethylene foam skin has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm. The laminated plastic film is heat bonded to a top surface of the polyethylene foam skin entirely and the laminated plastic film has a thickness in range of 0.03 to 0.3 mm. The plastic sheet is heat bonded to a bottom of the polyethylene foam skin entirely and the plastic sheet has a thickness in range of 0.3 to 2 mm. In addition, the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film. Alternatively, the polyethylene foam skin can be a multilayer foam skin and the laminated plastic film can be a patterned plastic film.

In another embodiment, a laminated layer for a slider of the present invention comprises a polyethylene foam skin and a laminated plastic film. The polyethylene foam skin has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm. The laminated plastic film is heat bonded to a top surface of the polyethylene foam skin entirely and the laminated plastic film has a thickness in range of 0.03 to 0.3 mm. In addition, the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film. Alternatively, the laminated plastic film is a patterned plastic film, which comprises an inner film and an outer film printed with patterns.

BRIEF DESCRIPTION OF DRAWINGS

The invention will be more clearly understood after referring to the following detailed description read in conjunction with the drawings wherein:

FIG. 1 is a perspective view of a first embodiment of the present invention;

FIG. 2 is a regionally enlarged cross sectional view of the first embodiment of the present invention;

FIG. 3 is an exploded prospective view of the first embodiment of the present invention;

FIG. 4 is a perspective view of a second embodiment of the present invention;

FIG. 5 is a cross sectional view of the second embodiment of the present invention;

FIG. 6 is a perspective view of a third embodiment of the present invention;

FIG. 7 is a perspective view of a fourth embodiment of the present invention; and

FIG. 8 is a cross sectional view of a fifth embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

A slider 1 according to a first embodiment of the present invention is shown in FIGS. 1 to 3. The slider 1 of the first embodiment comprises a polyethylene foam skin 10, a laminated plastic film 11 and a plastic sheet 12. The polyethylene foam skin 10 has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm. The laminated plastic film 11 is heat bonded to a top surface of the polyethylene foam skin 10 entirely and has a thickness in range of 0.03 to 0.3 mm. The plastic sheet 12 is heat bonded to a bottom of the polyethylene foam skin 10 entirely and has a thickness in range of 0.3 to 2 mm. In addition, the laminated plastic film 11 is formed with depressions 13 on both surfaces and the depressions 13 are distributed over the both surfaces of the laminated plastic film 11. More importantly, the depressions 13 of the laminated plastic film 11 facing to the polyethylene foam skin 10 are also heat bonded to the polyethylene foam skin 10, so as to enhance the bonding between the laminated plastic film 11 and the polyethylene foam skin 10, as shown in FIG. 2.

In the first embodiment of the present invention, the laminated plastic film 11 is a patterned film and comprises an inner film 110 and an outer film 111 as shown in FIG. 3. The inner film 110 is heat bonded to the polyethylene foam skin 10 entirely and has a thickness in range of 0.01 to 0.15 mm. Furthermore, the outer film 111 has a surface printed with patterns 2 thereon and the surface is heat bonded to the inner film 110 entirely, so as to cover the printed patterns 2, which are visible from outside of the outer film 111. Preferably, the outer film 111 has a thickness in range of 0.02 to 0.15 mm. Alternatively, the patterns 2 can also be printed an outer surface of the inner film 110 and the patterned outer surface of the inner film 110 is heat bonded to the outer film 111.

FIG. 4 and FIG. 5 show a slider 1 a as a second embodiment of the present invention. The slider 1 a comprises a first polyethylene foam skin 101, a second polyethylene foam skin 102, a laminated plastic film 11 a, and a plastic sheet 12 a. Similarly, the first polyethylene foam skin 101 and the second polyethylene foam skin 102 of the slider 1 a are the same as the polyethylene foam skin 10 of the slider 1 of the first embodiment, and have a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm respectively. The second polyethylene foam skin 102 is heat bonded to the first polyethylene foam skin entirely 101.

In addition, the laminated plastic film 11 a is heat bonded to the first polyethylene foam skin 101 entirely and has a thickness in range of 0.03 to 0.3 mm. The plastic sheet 12 a is heat bonded to the second polyethylene foam skin 102 entirely and has a thickness in range of 0.3 to 2 mm, similarly to the laminated plastic film 11 and the plastic sheet 12 of the first embodiment. The laminated plastic film 11 a of the second embodiment also is a patterned film as the foregoing laminated plastic film 11 of the first embodiment; therefore, the detailed description of the laminated plastic film 11 a is omitted.

FIG. 6 shows a laminated layer 3 as a third embodiment of the present invention. The laminated layer 3 is provided for heat bonding to a slider, such as foregoing described sliders made of foam skins or other sliders made of foam boards, so as to be a top layer of the slider. The laminated layer 3 of the third embodiment comprises a polyethylene foam skin 30 and a laminated plastic film 31. Similarly to the first and second embodiments of the present invention, the polyethylene foam skin 30 has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm. The laminated plastic film 31 is heat bonded to a top surface of the polyethylene foam skin 30 entirely and has a thickness in range of 0.03 to 0.3 mm. The laminated plastic film 31 also is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film 31. Furthermore, the laminated plastic film 31 also is a patterned plastic film, which has patterns 2 formed between an inner film and an outer film of the laminated plastic film 31.

More importantly, the laminated layer 3 of the third embodiment further comprises a bonding film 4, which is heat bonded to a bottom surface of the polyethylene foam skin 30 entirely. In operation, the bonding film 4 is preferably extruded and coated onto the polyethylene foam skin 30. Furthermore, the bonding film 4 is a copolymer, which mainly assists the laminated layer 3 to be heat bonded to a top of a slider, which is made of polystyrene foam board/core or other non-polyethylene foam board/core without adhesives. Therefore, the laminated layer 3 with the bonding film 4 of the present invention can be applied to various foam materials of sliders. In addition, the bonding film 4 has a thickness in range of 0.01 to 0.1 mm, preferably in range of 0.03 to 0.05 mm.

FIG. 7 shows a laminated layer 3 a as a fourth embodiment of the present invention. Similarly to the third embodiment, the laminated layer 3 a of the fourth embodiment is provided for being heat bonded to a bottom of a slider, which is made of foam materials, such as foam skins or boards/cores, so as to be a bottom layer of the slider. The laminated layer 3 a mainly comprises a polyethylene foam skin 30 a and a laminated plastic sheet 32. The polyethylene foam skin 30 a preferably has a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm, preferably a range of 4 to 8 PCF in the density and a range of 1 to 4 mm in the thickness. The laminated plastic sheet 32 is heat bonded to a top surface of the polyethylene foam skin 30 a entirely and has a thickness in range of 0.3 to 2 mm.

In addition, the laminated plastic sheet 32 comprises a laminated plastic film 31 a and a plate 32 a. The laminated plastic film 31 a is heat bonded to the top surface of the polyethylene foam skin 30 a and is a patterned plastic film, which has patterns 2 a formed between an inner film and an outer film of the laminated plastic film 31 as described in the above embodiments. Furthermore, the plate 32 a is heat bonded to the laminated plastic film 31 a and has a thickness in range of 0.3 to 2 mm. The plate 32 a is made of transparent materials; therefore, the patterns 2 a are visible from outside of the plate 32 a.

Similarly to the third embodiment, the laminated layer 3 a further comprises a bonding film 4 a, which is heat bonded to a bottom surface of the polyethylene foam skin 30 a entirely. The bonding film 4 a also is a copolymer, which assists the laminated layer 3 a to be heat bonded to the slider, which is made of polystyrene foam board/core or other non-polyethylene foam board/core without adhesives. In addition, the bonding film 4 a has a thickness in range of 0.01 to 0.1 mm, preferably in range of 0.03 to 0.05 mm.

FIG. 8 shows a fifth embodiment of the present invention and a further application of the third and fourth embodiments as well. The fifth embodiment shows a slider 5, which comprises a foam core 50, a laminated top layer 51 and a laminated bottom layer 52. The foam core 50 of the fifth embodiment is made of a non-polyethylene foam board, such as a polystyrene or polypropylene foam board, and the foam core 50 has a top surface and a bottom surface. Preferably, the foam core 50 has a density in the range of 0.8 to 8 PCF. In addition, the laminated top layer 51 is heat bonded to the top surface of the foam core 50 entirely and comprises a first polyethylene foam skin 510, a laminated plastic film 511 and a first bonding film 512. The laminated bottom layer 52 is heat bonded to the bottom surface of the foam core 50 entirely and comprises a second polyethylene foam skin 520, a laminated plastic sheet 521 and a second bonding film 522.

Substantially, the laminated top layer 51 of the fifth embodiment is the laminated layer 3 of the third embodiment, and the laminated bottom layer 52 is the laminated layer 3 a of the fourth embodiment. In addition, both the laminated plastic film 511 of the laminated top layer 51 and the laminated plastic sheet 521 of the laminated bottom layer 52 are patterned. Furthermore, the first bonding film 512 and the second bonding film 522 are provided for assisting the laminated top layer 51 and the laminated bottom layer 52 respectively to be heat bonded to the foam core 50, which is made of the non-polyethylene foam board/core, as described in the foregoing embodiments.

Numerous characteristics and advantages of the invention have been set forth in the foregoing description, together with details of the structure and function of the invention, and the novel features thereof are pointed out in appended claims. The disclosure, however, is illustrated only, and changes may be made in detail, especially, in matters of shape, size and arrangement of parts, materials and the combination thereof within the principle of the invention, to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed. 

1. A slider comprising: a polyethylene foam skin, having a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm; a laminated plastic film, heat bonded to a top surface of the polyethylene foam skin entirely, the laminated plastic film having a thickness in range of 0.03 to 0.3 mm, wherein the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film; and a plastic sheet, heat bonded to a bottom of the polyethylene foam skin entirely, the plastic sheet having a thickness in range of 0.3 to 2 mm.
 2. The slider of claim 1, wherein the laminated plastic film comprises: an inner film, heat bonded to the top of the polyethylene foam skin entirely, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 3. The slider of claim 1, wherein the laminated plastic film comprises: an inner film, having an inner surface heat bonded to the top of the polyethylene foam skin entirely, and an outer surface printed with patterns thereon, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the outer surface of the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 4. A slider comprising: a first polyethylene foam skin, having a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm; a second polyethylene foam skin, heat bonded to the first polyethylene foam skin entirely, the second polyethylene foam skin having a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm; a laminated plastic film, heat bonded to the first polyethylene foam skin entirely, the laminated plastic film having a thickness in range of 0.03 to 0.3 mm; and a plastic sheet, heat bonded to the second polyethylene foam skin entirely, the plastic sheet having a thickness in range of 0.3 to 2 mm.
 5. The slider of claim 4, wherein the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film.
 6. The slider of claim 4, wherein the laminated plastic film comprises: an inner film, heat bonded to the first polyethylene foam skin entirely, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 7. The slider of claim 4, wherein the laminated plastic film comprises: an inner film, having an inner surface heat bonded to the first polyethylene foam skin entirely, and an outer surface printed with patterns thereon, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the outer surface of the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 8. The slider of claim 5, wherein the laminated plastic film comprises: an inner film, heat bonded to the first polyethylene foam skin entirely, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 9. The slider of claim 5, wherein the laminated plastic film comprises: an inner film, having an inner surface heat bonded to the first polyethylene foam skin entirely, and an outer surface printed with patterns thereon, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the outer surface of the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 10. A laminated layer for a slider, the slider being made of foam materials and the laminated layer comprising: a polyethylene foam skin, having a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm; and a laminated plastic film, heat bonded to a top surface of the polyethylene foam skin entirely, the laminated plastic film having a thickness in range of 0.03 to 0.3 mm, wherein the laminated plastic film is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film.
 11. The laminated layer of claim 10, wherein the laminated plastic film comprises: an inner film, heat bonded to the top surface of the polyethylene foam skin entirely, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 12. The laminated layer of claim 10, wherein the laminated plastic film comprises: an inner film, having an inner surface heat bonded to the top surface of the polyethylene foam skin entirely, and an outer surface printed with patterns thereon, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the outer surface of the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 13. The laminated layer of claim 10, further comprising a bonding film heat bonded to a bottom surface of the polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the slider made of non-polyethylene foam materials and has a thickness in range of 0.01 to 0.1 mm.
 14. The laminated layer of claim 11, further comprising a bonding film heat bonded to a bottom surface of the polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the slider made of non-polyethylene foam materials and has a thickness in range of 0.01 to 0.1 mm.
 15. The laminated layer of claim 12, further comprising a bonding film heat bonded to a bottom surface of the polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the slider made of non-polyethylene foam materials and has a thickness in range of 0.01 to 0.1 mm.
 16. A laminated layer for a slider, the slider being made of foam materials and the laminated layer comprising: a polyethylene foam skin, having a density in a range of 1.5 to 12 PCF and a thickness in a range of 1 to 6 mm; and a laminated plastic sheet, heat bonded to a top surface of the polyethylene foam skin entirely, the laminated plastic sheet having a thickness in range of 0.3 to 2 mm.
 17. The laminated layer of claim 16, wherein the laminated plastic sheet comprises: a laminated plastic film, heat bonded to the top surface of the polyethylene foam skin, the laminated plastic film comprising: an inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm; and a plate, heat bonded to the laminated plastic film, wherein the plate has a thickness in range of 0.3 to 2 mm and the patterns are visible from outside of the plate.
 18. The laminated layer of claim 16, wherein the laminated plastic sheet comprises: a laminated plastic film, heat bonded to the top surface of the polyethylene foam skin and comprising: an inner film, having a surface printed with patterns thereon and the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the surface of the inner film entirely and the outer film having a thickness in range of 0.02 to 0.15 mm; and a plate, heat bonded to the laminated plastic film, wherein the plate has a thickness in range of 0.3 to 2 mm and the patterns are visible from outside of the plate.
 19. The laminated layer of claim 16, further comprising a bonding film heat bonded to a bottom surface of the polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the slider made of non-polyethylene foam materials and has a thickness in range of 0.01 to 0.1 mm.
 20. The laminated layer of claim 17, further comprising a bonding film heat bonded to a bottom surface of the polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the slider made of non-polyethylene foam materials and has a thickness in range of 0.01 to 0.1 mm.
 21. A slider comprising: a foam core, made of a non-polyethylene foam board, the foam core having a top surface and a bottom surface; a laminated top layer, heat bonded to the top surface of the foam core entirely, the laminated top layer comprising: a first polyethylene foam skin, having a top surface and a bottom surface; a laminated plastic film, heat bonded to the top surface of the first polyethylene foam skin entirely; and a first bonding film, heat bonded to the bottom surface of the first polyethylene foam skin entirely, wherein the bonding film is a copolymer provided for being heat bonded to the top of the foam core and has a thickness in range of 0.01 to 0.1 mm; and a laminated bottom layer, heat bonded to the bottom surface of the foam core entirely, the laminated bottom layer comprising: a second polyethylene foam skin, having a top surface and a bottom surface; a laminated plastic sheet, heat bonded to the top surface of the second polyethylene foam skin entirely; and a second bonding film, heat bonded to the bottom surface of the second polyethylene foam skin entirely, wherein the second bonding film is a copolymer provided for being heat bonded to the bottom of the foam core and has a thickness in range of 0.01 to 0.1 mm.
 22. The slider of claim 21, wherein the laminated plastic film of the laminated top layer comprises: an inner film, heat bonded to the top surface of the first polyethylene foam skin entirely, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, having a surface printed with patterns thereon, the surface being heat bonded to the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 23. The slider of claim 21, wherein the laminated plastic film of the laminated top layer comprises: an inner film, having an inner surface heat bonded to the top surface of the polyethylene foam skin entirely, and an outer surface printed with patterns thereon, the inner film having a thickness in range of 0.01 to 0.15 mm; and an outer film, heat bonded to the outer surface of the inner film entirely, wherein the outer film has a thickness in range of 0.02 to 0.15 mm and the patterns are visible from outside of the outer film.
 24. The slider of claim 21, wherein the laminated plastic film of the laminated top layer is formed with depressions on both surfaces and the depressions are distributed over the both surfaces of the laminated plastic film. 